新加坡\韩国\深圳杜邦PA66 101F塑胶原料注塑物性表：
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| DAM | 50%RH | |||||
| 基本性能 | 吸水率 | 24hr | ASTM D-570 | 1.2 | - | % |
| 密度 | --- | ASTM D-792 | 1.14 | - | g/cm3 | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.14 | - | --- |
| 模具收缩率 | --- | --- | 1.5 | - | % | |
| 阻燃性 | --- | UL 94 | 0.71 | - | mm | |
| 机械性能 | 拉伸强度 | --- | ASTM D-638 | 83 | 64 | MPa |
| 断裂拉伸强度 | --- | ASTM D-638 | 83 | - | MPa | |
| 断裂伸长率 | --- | ASTM D-638 | 50 | ＞300 | % | |
| 屈服伸长率 | --- | ASTM D-638 | 4 | - | % | |
| 弯曲模量 | --- | ASTM D-790 | 2800 | 1210 | MPa | |
| IZOD缺口冲击强度 | --- | ASTM D-256 | 53 | 105 | J/m | |
| 电气性能 | 表面电阻率 | --- | ASTM D-257 | 1014 | - | Ω |
| 体积电阻率 | --- | ASTM D-257 | 1015 | - | Ω.cm | |
| 介电强度 | 3.2mm | ASTM D-149 | 16.5 | - | kv/mm | |
| 介电强度 | 1.6mm | ASTM D-150 | 23.2 | - | kv/mm | |
| 介电常数 | 103Hz | ASTM D-150 | 4 | - | --- | |
| 介电常数 | 106Hz | ASTM D-150 | 3.7 | - | --- | |
| 损耗因数 | 102Hz | ASTM D-150 | 0.01 | - | --- | |
| 损耗因数 | 103Hz | ASTM D-150 | 0.02 | - | --- | |
| 损耗因数 | 106Hz | ASTM D-150 | 0.02 | - | --- | |
| 热 性 能 | 熔点 | --- | ASTM D-3418 | 262 | - | ℃ |
| 热变形温度 | 0.45MPa | ASTM D-648 | 210 | - | ℃ | |
| 热变形温度 | 1.80MPa | ASTM D-648 | 65 | - | ℃ | |